During the design and manufacturing process of Aerospace Micro Screws, floating material phenomenon is a common undesirable phenomenon in Aerospace Micro Screws, which can easily lead to serious defects or even scrapping of Aerospace Micro Screws.
TA2 pure titanium outer hexagon M3 (Ti)
There are many reasons for the generation of floating materials, so there are many solutions. Today, we will discuss the types of floating materials in Aerospace Micro Screws. For floating materials, they can be divided into three types according to their size and formation factors.
One of the types of floating materials is the rising phenomenon of stamping waste: waste refers to the part separated from the product during a stamping process. Its size is usually the same as the shape of the edge of the lower die.
Its scope and harm are the largest of the three phenomena. When this phenomenon occurs, it may cause the punch or blade to crack or even break, it may cause the guide pin of the Aerospace Micro Screws to break, and it may also cause the template to crack and the mold to explode.
The second type of Aerospace Micro Screws floating material is the rising phenomenon of stamping waste, which refers to non-integral products or non-integral waste generated in a process. Its size is relatively small, such as the formation of product burrs falling off; stamping waste filaments, etc.
Contact Us

Author:

Mr. yjfastener

E-mail:

hou@citool.com

Phone/WhatsApp:

+8615826187211

Popular Products
You may also like
Related Categories

Email to this supplier

Subject:
Email:
Message:

Your message must be betwwen 20-8000 characters

We will contact you immediately

Fill in more information so that we can get in touch with you faster

Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.

Send